A team of researchers from Chinese Academy of Sciences (CAS) presented a facile approach to prepare open-cell polypropylene (PP)/starch blend foams with low density by twin-screw extrusion using water as a physical blowing agent and starch as an effective water carrier. The cell diameter of the prepared PP/starch blend foams was controlled by using different nucleating agents and changing the die geometry.

Foams with mean cell diameter in the range of 0.4-4.5 mm and open-cell content larger than 90% were successfully obtained. Moreover, a remarkable improvement of hydrophobicity of the foams was obtained when decreasing the cell diameters. Consequently, the water contact angle and oil recovery efficiency were increased up to 142.2° and 98.4%, respectively, when the mean cell diameter was reduced to 0.4 mm. These characteristics make this foam a promising candidate absorbent material for use in oil-spill cleanup.